MS 20 Hybrid Sealant
Description
Low Modulus Sealant based on MS polymer. Product has low module and high elasticity after curing. MS 20 is specially designed to seal expansion joints in facades.
Hoiatus: Järgige igal juhul toote etiketil esitatud teavet.
Benefits
Low Modulus, class 25 LM
High elasticity
Phthalate free
UV resistant
Can be painted (possibility of painting even uncured sealant)
Neutral, non-corrosive to metals and applicable on alkaline surfaces
Can be applied indoor and outdoor
100% compatible with acrylic sealants
Applications
Sealing expansion joints in facades
Filling gaps, joints, slots in concrete, wood, gypsum, masonry and other building materials
Sealing skirting-boards, panels, plates made of synthetic materials, glaze, terracotta, elements made of synthetic materials, wood, metals, metal plates, for all types of surfaces in building such as brick, concrete, gypsum, plasters
Technical parameters
Application temperature:
+5°C to +50°C
Modulus 100% (ISO 37):
0,5 MPa
Skin formation time:
20–40 min
Curing rate:
2–3 mm/ 24 h
Tensile strength (ISO 37):
1 MPa
Elongation at break (ISO 37):
300%
Shore A hardness (ISO 868):
22–30
Movement accommodation:
25%
Temperature resistance after curing:
-40°C to +90°C
Logistic table
| Product name Vastavatele tootevariantidele määratud unikaalne kood, mis määrab kindlaks nende mahutavuse, suuruse ja värvid. | Content | Packaging | Pieces per box | Pieces per pallet | Colours |
|---|---|---|---|---|---|
| Low Modulus MS Sealant | 600 ml | Foil | 12 | 1 152 | Grey |
Sarnased kategoorias
PU 25 Polyurethane Sealant
Loe rohkem
MS 20 Hybrid Sealant
Loe rohkem
PU 40 Polyurethane Sealant
Loe rohkem
Kas teil on toote kohta küsimusi?
Ei leidnud veebisaidilt infot, soovite rohkem teada?
Saada meile oma päring ja meie spetsialist vastab teile.